NO. | Test Items | Values | |
|---|---|---|---|
| 1 | Before ageing test | 1.1 Tensile strength(MPa) | ≥5.0 |
| 1.2 Elongation at break(%) | ≥200 | ||
| 2.1 Test condition | 135±2℃/168h | ||
| 2.2 Tensile strength(MPa) | ≥5.0 | ||
| 2.3 Tensile strength rate(%) | |||
| 2.4 Elongation at break rate (%) | ±40 | ||
| 3 | Air bomb ageing test | 3.1 Test condition | 127±2℃/40h |
| 3.2 Tensile strength rate(%) | ±30 | ||
| 3.3 Elongation at break rate (%) | ±30 | ||
| 4 | 4.1 Test condition | ||
| 4.2 Loading elongation rate(%) | < 100 | ||
| 4.3 Un-loading elongation rate(%) | < 25 | ||
| 5 | Ozone ageing test | 5.1 Test condition | |
| 5.2 Test result | No cracks | ||
| 5.3 Test condition | 40±2℃/72h, concentration 200±50ppm | ||
| 5.4 Test result | |||
| 6 | Low-temperature bend test | 6.1 Test condition | -35±2℃ |
| 6.2 Low-temperature elongation at unbreak(%) | > 30 | ||
| 6.3 Wire surface after low-temperature bend | No cracks | ||
| Maximum material operating temperature | 90℃ | ||